Mold Max™ Silicones are tin-cured silicone rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silcones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.
Features
- Mold Max™ Silicones will reproduce the finest detail and are suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements.
- Mold Max™ 30 can be thickened with THI-VEX™ additive for brush-on applications.
- Mold Max™ Silicones can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins (without using a release agent).
Data At-A-Glance
| Mix Ratio By Weight | 100A:10B |
| Specific Gravity | 1.18 g/cc |
| Specific Volume | 23.5 cu. in./lb. |
| Color | Pink |
| Shore Hardness | 30 A |
| Tensile Strength | 577 psi |
| 100% Modulus | 110 psi |
| Elongation @ Break | 300 % |
| Die B Tear Strength | 125 pli |
| Shrinkage | 0.002 in. / in. |
| Pot Life | 45 minutes |
| Cure Time | 24 hours |
| Useful Temperature (max) | 400 °F |
| Useful Temperature (min) | -65 °F |
| Mixed Viscosity | 25,000 cps |
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Smooth-On Mold Max 30
Smooth-On Mold Max 30
Mold Max™ Silicones are tin-cured silicone rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silcones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.
Features
- Mold Max™ Silicones will reproduce the finest detail and are suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements.
- Mold Max™ 30 can be thickened with THI-VEX™ additive for brush-on applications.
- Mold Max™ Silicones can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins (without using a release agent).
Data At-A-Glance
| Mix Ratio By Weight | 100A:10B |
| Specific Gravity | 1.18 g/cc |
| Specific Volume | 23.5 cu. in./lb. |
| Color | Pink |
| Shore Hardness | 30 A |
| Tensile Strength | 577 psi |
| 100% Modulus | 110 psi |
| Elongation @ Break | 300 % |
| Die B Tear Strength | 125 pli |
| Shrinkage | 0.002 in. / in. |
| Pot Life | 45 minutes |
| Cure Time | 24 hours |
| Useful Temperature (max) | 400 °F |
| Useful Temperature (min) | -65 °F |
| Mixed Viscosity | 25,000 cps |
Original: $39.50
-70%$39.50
$11.85Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
Mold Max™ Silicones are tin-cured silicone rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silcones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.
Features
- Mold Max™ Silicones will reproduce the finest detail and are suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements.
- Mold Max™ 30 can be thickened with THI-VEX™ additive for brush-on applications.
- Mold Max™ Silicones can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins (without using a release agent).
Data At-A-Glance
| Mix Ratio By Weight | 100A:10B |
| Specific Gravity | 1.18 g/cc |
| Specific Volume | 23.5 cu. in./lb. |
| Color | Pink |
| Shore Hardness | 30 A |
| Tensile Strength | 577 psi |
| 100% Modulus | 110 psi |
| Elongation @ Break | 300 % |
| Die B Tear Strength | 125 pli |
| Shrinkage | 0.002 in. / in. |
| Pot Life | 45 minutes |
| Cure Time | 24 hours |
| Useful Temperature (max) | 400 °F |
| Useful Temperature (min) | -65 °F |
| Mixed Viscosity | 25,000 cps |